Silver brazing nickel plate
#1
Senior Member
Thread Starter
Silver brazing nickel plate
I recently had a head badge made in nickel because I had heard it's easier to curve than stainless around a head tube but have recently heard that I'll need to remove the nickle plating before brazing.
I'm very uneducated when it comes to the different types of metal and their ability to braze.
Do I need to remove anything or can I simply sand it down like a normal? Or do I need to have the badges made in stainless?
Thanks in advance.
Brandon
I'm very uneducated when it comes to the different types of metal and their ability to braze.
Do I need to remove anything or can I simply sand it down like a normal? Or do I need to have the badges made in stainless?
Thanks in advance.
Brandon
#2
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
I didnt check into it too far, but the first thing I saw said it's never a good idea to braze to plating.
I am curious if I understand what you had made, can you link to the material? Is it nickel plated steel?
I am curious if I understand what you had made, can you link to the material? Is it nickel plated steel?
#3
Senior Member
Thread Starter
I don't have a link since it was done locally, but I believe it to be nickel plated steel.
#4
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
My only experience with nickel plating was an electroless nickel plated sensor target I had to machine. That stuff is really soft. My impression is that it wouldn't be happy to be brazed. It would work great if you were bolting the head badge on. We had the target plated so it wouldn't corrode.
#5
Senior Member
Join Date: Nov 2014
Location: Eugene, Oregon, USA
Posts: 27,547
Mentioned: 217 Post(s)
Tagged: 0 Thread(s)
Quoted: 18354 Post(s)
Liked 4,502 Times
in
3,346 Posts
@gugie had successfully brazed a steer tube into a chromed fork crown using A LOT OF FLUX. I don't know if the crown was triple plated or not.
You may be able to do the same with silver solder and Nickel, being very careful with the temperature.
HOWEVER, you have a non-structural part. There are some excellent adhesives that you can use. Talk to a good vintage auto detail shop. I don't remember the brand, but the window felt adhesive I got a while ago was really good.
And, then you have the advantage of being able to paint your frame first, then simply glue the badge on. No need for careful masking.
You may be able to do the same with silver solder and Nickel, being very careful with the temperature.
HOWEVER, you have a non-structural part. There are some excellent adhesives that you can use. Talk to a good vintage auto detail shop. I don't remember the brand, but the window felt adhesive I got a while ago was really good.
And, then you have the advantage of being able to paint your frame first, then simply glue the badge on. No need for careful masking.
#6
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,056
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4195 Post(s)
Liked 3,837 Times
in
2,295 Posts
So confusion as to why it would be assumed that a nickel plated steel would be much easier to bend then an unplated steel of similar thickness?
I think one concern about brazing onto a plated frame is the gas that might "boil off" if the acid etching solutions were not completely removed after the plating was done. Have to admit I know little about plating's tensile strength WRT it's attachment to the surface (steel). Andy
I think one concern about brazing onto a plated frame is the gas that might "boil off" if the acid etching solutions were not completely removed after the plating was done. Have to admit I know little about plating's tensile strength WRT it's attachment to the surface (steel). Andy
__________________
AndrewRStewart
AndrewRStewart
Likes For Andrew R Stewart:
#7
Bike Butcher of Portland
Join Date: Jul 2014
Location: Portland, OR
Posts: 11,630
Bikes: It's complicated.
Mentioned: 1299 Post(s)
Tagged: 0 Thread(s)
Quoted: 4677 Post(s)
Liked 5,790 Times
in
2,279 Posts
@gugie had successfully brazed a steer tube into a chromed fork crown using A LOT OF FLUX. I don't know if the crown was triple plated or not.
Brazing something like a badge to a frame is damn hard, molten silver is pretty damn slippery.
Just epoxy it on after painting.
__________________
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
#8
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
Seems like Trek used a kind of mastic to glue their head badges on. That was after my time, we were using screws when I was there.
#9
Senior Member
Join Date: Dec 2019
Posts: 954
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 321 Post(s)
Liked 263 Times
in
212 Posts
Yes my ill-fated circa 2008 Trek 520 had some kind of schmoo holding the headbadge on. Its Chinese replacement didn't even get a headbadge, just a painted-logo of some sort. I guess if you can save a few more cents a frame it all adds up to bigger yachts for the execs.
#10
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,056
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4195 Post(s)
Liked 3,837 Times
in
2,295 Posts
To be clear, I reamed the fork crown, then silver brazed the steerer, no chrome was brazed to. The LOT OF FLUX was dried onto the chromed fork crown to protect the chrome.
I silver brazed some brass 531 badges onto a frame once. Showed them off to Jamie Swann at French Fender Day a couple of years ago. He asked why I didn't just epoxy them on. I waited a count or two, then gave myself a good dope slap in the forehead.
Brazing something like a badge to a frame is damn hard, molten silver is pretty damn slippery.
Just epoxy it on after painting.
I silver brazed some brass 531 badges onto a frame once. Showed them off to Jamie Swann at French Fender Day a couple of years ago. He asked why I didn't just epoxy them on. I waited a count or two, then gave myself a good dope slap in the forehead.
Brazing something like a badge to a frame is damn hard, molten silver is pretty damn slippery.
Just epoxy it on after painting.
__________________
AndrewRStewart
AndrewRStewart
#11
Bike Butcher of Portland
Join Date: Jul 2014
Location: Portland, OR
Posts: 11,630
Bikes: It's complicated.
Mentioned: 1299 Post(s)
Tagged: 0 Thread(s)
Quoted: 4677 Post(s)
Liked 5,790 Times
in
2,279 Posts
Sure, but... I guess how and why one attaches a badge is a choice that reflects their approach to building in general. My take has been to produce a frame that could out last me. My marking my creation is one part of that. Having worked on hundreds of bikes that lack badging, branding or decals and the hours I've wondered about the bikes' lost identities just reinforced my view, I want my mark to not be trusted to a future hack refinisher. So I first silvered on my "S" made from electrical wire bent around the vise handle. After a couple dozen+ frames i decided that it was time for a more elegant mark. Now I have my "S" water jetted from SS plate. and still silver them on. Andy
__________________
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
#12
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
I put a 'K' on my seat tube, it really stiffened it up and made it so I felt a lot better putting it in a stand when I needed to do that. But that seat tube died in a failed attempt to remove the seat post, so the replacement isn't getting that feature. I found it to be a pain to braze them on and also masking is a pain, so I'm probably not doing that again. Probably
I am conflicted about putting it on a top or down tube. Looks nice, but why anneal that much of the tube?
I am conflicted about putting it on a top or down tube. Looks nice, but why anneal that much of the tube?
#13
Senior Member
Thread Starter
Sure, but... I guess how and why one attaches a badge is a choice that reflects their approach to building in general. My take has been to produce a frame that could out last me. My marking my creation is one part of that. Having worked on hundreds of bikes that lack badging, branding or decals and the hours I've wondered about the bikes' lost identities just reinforced my view, I want my mark to not be trusted to a future hack refinisher. So I first silvered on my "S" made from electrical wire bent around the vise handle. After a couple dozen+ frames i decided that it was time for a more elegant mark. Now I have my "S" water jetted from SS plate. and still silver them on. Andy
My thought on curving was that I know SS to be a bit more brittle and harder to curve than a mild steel. At least that's been my experience with it. I could easily get some badges cut in SS as I had this one done with a water jet.
I'll get a picture up today.
#14
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
I think I got 316 stainless .03" thick. Can cut it with scissors. Bends fine.
Likes For unterhausen:
#15
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,056
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4195 Post(s)
Liked 3,837 Times
in
2,295 Posts
It's hard enough to get my "S" centered and straight. Andy
__________________
AndrewRStewart
AndrewRStewart
#16
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,056
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4195 Post(s)
Liked 3,837 Times
in
2,295 Posts
Andy, what thickness SS do you use for your badges?
My thought on curving was that I know SS to be a bit more brittle and harder to curve than a mild steel. At least that's been my experience with it. I could easily get some badges cut in SS as I had this one done with a water jet.
I'll get a picture up today.
My thought on curving was that I know SS to be a bit more brittle and harder to curve than a mild steel. At least that's been my experience with it. I could easily get some badges cut in SS as I had this one done with a water jet.
I'll get a picture up today.
As to the bendability of SS plate. The .040+ thickness I've used is no problem. There are no creases or corners, in the bending, so no real chance to crack or have less the square corners. But if a badge were to have a relief or carved surface it would likely be thicker and the thick/thin differences might well provide an uneven bending. For this reason if major surface texture is wanted consider carving from a tube of casting. Andy
__________________
AndrewRStewart
AndrewRStewart
#17
Senior Member
Thread Starter
So here's a picture of my head badge in question. You can see it has a somewhat glossy finish to it on this side. It isn't this way on the other side however. It's 0.064 thick and I was going to attempt to curve it around a 36mm head tube. Although I think I'd rather have it be somewhere closer to 0.040.
Think curving will be doable?
Think curving will be doable?
#18
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
That seems a bit stout, but there is no harm in trying. I think for something that thick I might use something to form it into shape
That looks nice.
That looks nice.
#19
Senior Member
Thread Starter
Thanks! Yeah that's about what I was thinking as well. I think I have another spot on a frame that I can put it and curve it. I'll have to have some thinner pieces made....in stainless this time.
#20
Senior Member
Join Date: Nov 2014
Location: Eugene, Oregon, USA
Posts: 27,547
Mentioned: 217 Post(s)
Tagged: 0 Thread(s)
Quoted: 18354 Post(s)
Liked 4,502 Times
in
3,346 Posts
Any pieces of heavy plumbing pipe, or solid steel you could use if it takes more force to bend than you can get with your hands?
#21
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
So you mechanically removed the old steerer? I botched a steerer re-thread and have decided to replace it. I was thinking about sweating it out, but I'm not positive that's a good approach
#22
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,056
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4195 Post(s)
Liked 3,837 Times
in
2,295 Posts
0.064" thick is pretty thick for such a small width of surface, to bend and have the bends "take" to the edges. Next time I would consider carving a pre bent piece, a tube section perhaps. Andy
__________________
AndrewRStewart
AndrewRStewart
#23
Bike Butcher of Portland
Join Date: Jul 2014
Location: Portland, OR
Posts: 11,630
Bikes: It's complicated.
Mentioned: 1299 Post(s)
Tagged: 0 Thread(s)
Quoted: 4677 Post(s)
Liked 5,790 Times
in
2,279 Posts
First time I did this was on a "found" Paramount by @RiddleOfSteel. I used a 7/8" step drill to come at it from both sides, leaving ~1/16" of material, then used a large rat tail file to get down to where I could see the brass colored filler, then carefully filed and sanded it down the fork crown to fit up a new steerer. It wasn't perfectly round from that operation, but quite close enough to silver braze in a new steerer. I've since performed this operation on two more forks successfully. It's a lot of elbow grease. One fork had a particularly hard steerer, so I used a hacksaw to score it into sections so I can heat small areas at a time to remove them.. No way you can sweat out a steerer intact without worrying about the effect on the blade/fork connection.
I've since found a 25mm step drill, which would leave a lot less material to file out at the end.
__________________
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
#24
Randomhead
Join Date: Aug 2008
Location: Happy Valley, Pennsylvania
Posts: 24,387
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4 Post(s)
Liked 3,687 Times
in
2,510 Posts
Okay, thanks. The thread is mostly okay, but it tore in one place and that is exactly where the top cup sits. Probably okay, but I would rather fix it. The original sin was not checking the steerer length before I put it in. Threadless steerers have spoiled me.
#25
framebuilder
Two pieces of 4130 tubing with a wall thickness of 0.120" can be used to bend/curve cut out flat plate to fit around a frame tube. The inside tube would have an OD the size of the head or seat tube. Because of spring back it is probably better for it to be 1/8" smaller. The outside tube would have an OD 1/4" larger. This makes its ID about the same as the OD of the inner tube. The outside tube is cut in half lengthwise so it will fit against the inside tube. The design is placed between the 2 tubes and squeezed together in a vise.
I've shown this picture in several posts but i will do it here again. My frame building class student cut his Michigan shaped design out of flat stainless steel plate and squeezed it between 2 tubes as described above before brazing it onto his seat tube. As a substitute, 0.058" could be used. There might be some risk of ovalizing the tubes (which might not matter). I had .120" tubing so there wasn't a reason to use 0.058".
I've shown this picture in several posts but i will do it here again. My frame building class student cut his Michigan shaped design out of flat stainless steel plate and squeezed it between 2 tubes as described above before brazing it onto his seat tube. As a substitute, 0.058" could be used. There might be some risk of ovalizing the tubes (which might not matter). I had .120" tubing so there wasn't a reason to use 0.058".