This frame is goner?
Picked this up for parts, but hard to believe this is all it takes to salvage a carbon frame. Looks like something fell on the top tube, chipping and cracking the paint, still not a crash. Any way to save this?
#2
Senior Member
Join Date: Apr 2016
Posts: 1,236
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 503 Post(s)
Liked 436 Times
in
335 Posts
Hard to tell from the pictures, I'd chip off as much paint as I could to get a better view of the carbon: lighter lines equals delamination, but there could be other damage you can't see - it needs an ultrasound scan. Any carbon frame is fixable if you spend enough, but often not really worth it. This is the price you pay for high performance plastic - that ding in a steel frame would just be annoying.
Likes For grumpus:
#3
Senior Member
Join Date: Aug 2009
Posts: 2,395
Mentioned: 14 Post(s)
Tagged: 0 Thread(s)
Quoted: 1562 Post(s)
Liked 1,734 Times
in
974 Posts
Just like with any boat hull or any other composite object: use a hard object to tap along the carbon top tube. It should have a hard crisp knock to it. When you get to that chipped section, does the tone change? If there is no change in tone then I would say it's totally fine. If it turns into a thud then there is de-lamination.
Likes For icemilkcoffee:
#4
Senior Member
Join Date: Feb 2012
Location: Rochester, NY
Posts: 18,096
Bikes: Stewart S&S coupled sport tourer, Stewart Sunday light, Stewart Commuting, Stewart Touring, Co Motion Tandem, Stewart 3-Spd, Stewart Track, Fuji Finest, Mongoose Tomac ATB, GT Bravado ATB, JCP Folder, Stewart 650B ATB
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 4210 Post(s)
Liked 3,878 Times
in
2,315 Posts
If the frame construction allows a borescope up inside the tube I would suggest that as an inspection method that shouldn't cost too much. (I know a couple of auto body work guys that use them for unibody inspections).
The tapping the surface with a hard object is ok but the paint can delam. from the structural carbon and you'll just feel that change. I agree with grumpus's suggestion of removing paint to better see/tap the structural carbon.
There are a number of outfits that fix carbon bike frames. Most will provide a starting assessment via photos in an email and modify as needed when they get hands on. Most likely will also offer paint touch up services (were I them I would only offer repairs that also included the paint work). Costs from a few hundred $ and up are typical (not including shipping).
The tapping the surface with a hard object is ok but the paint can delam. from the structural carbon and you'll just feel that change. I agree with grumpus's suggestion of removing paint to better see/tap the structural carbon.
There are a number of outfits that fix carbon bike frames. Most will provide a starting assessment via photos in an email and modify as needed when they get hands on. Most likely will also offer paint touch up services (were I them I would only offer repairs that also included the paint work). Costs from a few hundred $ and up are typical (not including shipping).
__________________
AndrewRStewart
AndrewRStewart
Likes For Andrew R Stewart:
#5
Full Member
Thread Starter
Join Date: Mar 2013
Location: Albany, NY
Posts: 420
Bikes: Trek FX 7.3, Specialized Roubaix, Orbea Terra, Aostimotor S17 ebike, Huffy RedRock (first bike)
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 205 Post(s)
Liked 268 Times
in
134 Posts
Great idea, I have one, and finally reason to put it to use.
Likes For XxHaimBondxX:
#6
Senior Member
Join Date: Jul 2006
Location: San Jose (Willow Glen) Ca
Posts: 9,847
Bikes: Kirk Custom JK Special, '84 Team Miyata,(dura ace old school) 80?? SR Semi-Pro 600 Arabesque
Mentioned: 106 Post(s)
Tagged: 0 Thread(s)
Quoted: 2338 Post(s)
Liked 2,827 Times
in
1,543 Posts
hard to tell, but it appear to be a serious hit that caused frame to deform in a good sized area with all the paint chips and all. I think I see some fiber ends, but not sure
all in all seems a bit suspect
if is it a good frame expect 300 to 600+ for a repair
I have not used any of these, but the calfee is well known.... the first two are near me san jose, santa cruz area the third in Minnesota and the last might of interest to OP XxHaimBondxX in that it is in NY State just up the road from albany
https://calfeedesign.com/carbon-repair/
https://www.spydercomposites.com/faqs
https://www.applemanbicycles.com/repair/
https://carbonbikespecialists.com/?useYB=1
all in all seems a bit suspect
if is it a good frame expect 300 to 600+ for a repair
I have not used any of these, but the calfee is well known.... the first two are near me san jose, santa cruz area the third in Minnesota and the last might of interest to OP XxHaimBondxX in that it is in NY State just up the road from albany
https://calfeedesign.com/carbon-repair/
https://www.spydercomposites.com/faqs
https://www.applemanbicycles.com/repair/
https://carbonbikespecialists.com/?useYB=1
__________________
Life is too short not to ride the best bike you have, as much as you can
(looking for Torpado Super light frame/fork or for Raleigh International frame fork 58cm)
Life is too short not to ride the best bike you have, as much as you can
(looking for Torpado Super light frame/fork or for Raleigh International frame fork 58cm)
Last edited by squirtdad; 02-06-24 at 03:22 PM.
Likes For squirtdad:
#7
Senior Member
Join Date: Apr 2009
Location: New Rochelle, NY
Posts: 38,725
Bikes: too many bikes from 1967 10s (5x2)Frejus to a Sumitomo Ti/Chorus aluminum 10s (10x2), plus one non-susp mtn bike I use as my commuter
Mentioned: 140 Post(s)
Tagged: 1 Thread(s)
Quoted: 5793 Post(s)
Liked 2,585 Times
in
1,433 Posts
The paint cracks are a good indication of compromised CF structure, but indications are more by way of warning than proof.
Paint is often more brittle than and cannot flex as much as the thin structure they cover. If you can flake off more paint you might be able to verify whether there's visible damage to the CF or, more commonly, the matrix holding it together. Sometimes, if you have well calibrated fingers, you can tell by gently squeezing the area and a comparable one nearby feeling for a softer spot. As noted, the tap test may also offer clues.
However, while it's easy to confirm damage, there is virtually no way to confirm that a CF structure is undamaged, shy of expensive testing methods. So, the best you can hope for is either positive confirmation that it's toast, or accepting that it seems OK and deciding whether seems OK is good enough.
Paint is often more brittle than and cannot flex as much as the thin structure they cover. If you can flake off more paint you might be able to verify whether there's visible damage to the CF or, more commonly, the matrix holding it together. Sometimes, if you have well calibrated fingers, you can tell by gently squeezing the area and a comparable one nearby feeling for a softer spot. As noted, the tap test may also offer clues.
However, while it's easy to confirm damage, there is virtually no way to confirm that a CF structure is undamaged, shy of expensive testing methods. So, the best you can hope for is either positive confirmation that it's toast, or accepting that it seems OK and deciding whether seems OK is good enough.
__________________
FB
Chain-L site
An ounce of diagnosis is worth a pound of cure.
Just because I'm tired of arguing, doesn't mean you're right.
“One accurate measurement is worth a thousand expert opinions” - Adm Grace Murray Hopper - USN
WARNING, I'm from New York. Thin skinned people should maintain safe distance.
FB
Chain-L site
An ounce of diagnosis is worth a pound of cure.
Just because I'm tired of arguing, doesn't mean you're right.
“One accurate measurement is worth a thousand expert opinions” - Adm Grace Murray Hopper - USN
WARNING, I'm from New York. Thin skinned people should maintain safe distance.
Likes For FBinNY:
#8
Senior Member
Join Date: Apr 2016
Posts: 1,236
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 503 Post(s)
Liked 436 Times
in
335 Posts
Just like with any boat hull or any other composite object: use a hard object to tap along the carbon top tube. It should have a hard crisp knock to it. When you get to that chipped section, does the tone change? If there is no change in tone then I would say it's totally fine. If it turns into a thud then there is de-lamination.
#9
I am potato.
Join Date: Jun 2015
Location: Pacific Northwest
Posts: 3,116
Bikes: Only precision built, custom high performance elitist machines of the highest caliber. 🍆
Mentioned: 29 Post(s)
Tagged: 0 Thread(s)
Quoted: 1790 Post(s)
Liked 1,631 Times
in
934 Posts
It's hard to tell exactly what kind of bike this is. My spide-y sense tells me it is the result of high impact with a handlebar or perhaps the full force of a fall over against a post or similar at just the right distance to nearly wedge before stopping. (I once had that exact situation with an aluminum top tube.)
In any case, what you have is pretty darn rare in spite of what the crabon-plastique detractors will suggest.
When I wedged a cadence sensor between the thinnest midspan portion of the chain stay and the crank arm. The tap test told me is was damaged. I still rode it for months until a bubble formed. Ruckus Composites repaired it including factory paint for ~$800.
Worth every penny. Seamless and indistinguishable...Well, I can tell because I know the area and how to actually perform the repair. But, nobody else can tell & the frame was worth the cost to me to have it professionally done.
Carbon can be repaired effectively as many times as needed in whatever manner needed with out loss of performance. The question is always cost. For the Cervelo, with factory paint, $800 was a no-brainer. A standard $5-600 repair with flat-black paint would've sucked too much value from the bike on account of the repair being both obvious and ugly.
If the frame is worth $5-600 and all the trouble to box/ship/etc... to you, go for it.
In any case, what you have is pretty darn rare in spite of what the crabon-plastique detractors will suggest.
When I wedged a cadence sensor between the thinnest midspan portion of the chain stay and the crank arm. The tap test told me is was damaged. I still rode it for months until a bubble formed. Ruckus Composites repaired it including factory paint for ~$800.
Worth every penny. Seamless and indistinguishable...Well, I can tell because I know the area and how to actually perform the repair. But, nobody else can tell & the frame was worth the cost to me to have it professionally done.
Carbon can be repaired effectively as many times as needed in whatever manner needed with out loss of performance. The question is always cost. For the Cervelo, with factory paint, $800 was a no-brainer. A standard $5-600 repair with flat-black paint would've sucked too much value from the bike on account of the repair being both obvious and ugly.
If the frame is worth $5-600 and all the trouble to box/ship/etc... to you, go for it.
__________________
I shouldn't have to "make myself more visible;" Drivers should just stop running people over.
Car dependency is a tax.
I shouldn't have to "make myself more visible;" Drivers should just stop running people over.
Car dependency is a tax.
Likes For base2:
#10
I'm good to go!
Join Date: Jul 2017
Location: Mississippi
Posts: 14,992
Bikes: Tarmac Disc Comp Di2 - 2020
Mentioned: 51 Post(s)
Tagged: 0 Thread(s)
Quoted: 6196 Post(s)
Liked 4,811 Times
in
3,319 Posts
It isn't a big deal. A person that has the skills can fix that carbon fiber just as someone that has the skills to braze on a steel bike. What is a big deal is finding those people that have the skills. They are out there. But they'll probably want more for that repair than you'll want to pay. Just like most people that braze will probably want more to replace a tube on a bike than you'll be willing to pay. But if you have any skills with glass work for things made of fiber glass, you can probably figure out and get the stuff you need to do a decent repair on CF yourself.
Though depending on the extent of the damage, it might not be worth the time and effort.
Though depending on the extent of the damage, it might not be worth the time and effort.
#11
Senior Member
Last year I acquired a Giant OCR frame that had a heavy tube fall on the top tube and crushed the carbon. I was able to flex the tube in that area with my fingers and the tap test with a quarter also showed damage. Although have never worked with carbon I did the repair myself with carbon fabric procured from Amazon. Turned out fine structurally, but cosmetically it was ugly! I gave it to a guy who is still riding it.
Likes For TiHabanero:
#12
Senior Member
Join Date: May 2019
Location: Bloomington, IN
Posts: 2,951
Bikes: Paramount, Faggin, Ochsner, Ciocc, Basso
Mentioned: 117 Post(s)
Tagged: 0 Thread(s)
Quoted: 1303 Post(s)
Liked 1,912 Times
in
1,142 Posts
In my mind this frame is done. What we found out at Indy Car when CF first came out they tested it with a sledge hammer. And the results found spider cracks in the tub after the testing. So I would suspect the same here. I normally do work with CF golf shafts as a Golf Equipment Professional, and any damage like this would test my liability insurance if I let it back out into the wild. If anyone wants to try to save it I would give caution about further failure. One of those ride at your own risk cases. JMHO, MH
#13
Senior Member
Join Date: Oct 2023
Location: New Jersey
Posts: 571
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 366 Post(s)
Liked 274 Times
in
175 Posts
Just like with any boat hull or any other composite object: use a hard object to tap along the carbon top tube. It should have a hard crisp knock to it. When you get to that chipped section, does the tone change? If there is no change in tone then I would say it's totally fine. If it turns into a thud then there is de-lamination.
#14
Senior Member
Join Date: Sep 2017
Posts: 7,887
Mentioned: 38 Post(s)
Tagged: 0 Thread(s)
Quoted: 6972 Post(s)
Liked 10,971 Times
in
4,692 Posts
Looks like paint damage. I'd still be riding it.
cf is not as fragile as people like to believe.
cf is not as fragile as people like to believe.
#15
Senior Member
Join Date: Apr 2010
Location: Elevation 666m Edmonton Canada
Posts: 2,483
Bikes: 2013 Custom SA5w / Rohloff Tourster
Mentioned: 7 Post(s)
Tagged: 0 Thread(s)
Quoted: 1237 Post(s)
Liked 324 Times
in
249 Posts
Since you bought it for scrap there is NO reason to fix it. It looks like it's 15 or 20 years old at least anyway. The tube looks mostly round, old design.
The whole white part looks dented to me.
The whole white part looks dented to me.
#16
Senior Member
Disclaimer: Everything is at your own risk.
I would first check softness with thumb, compared to surroundings. Soft? Fail. Still feels rigid? Proceed to next test.
Tap test like others have said. Sound OK?
Borescope would be good, to see if cracks extend to inside the tube.
Then I would carefully chip off paint, examine, then touch up the paint. But perhaps not if it passes all above tests.
Part of the reason I am saying the above is that the top tube is not the highest stressed part of the frame, and that's a pretty fat tube. That kind of damage on skinny chainstay or seatsay, would be more critical. Not saying the above is "fine", but you have a bit more margin.
What style of bike is it? Road? Mountain? Downhill?
I would first check softness with thumb, compared to surroundings. Soft? Fail. Still feels rigid? Proceed to next test.
Tap test like others have said. Sound OK?
Borescope would be good, to see if cracks extend to inside the tube.
Then I would carefully chip off paint, examine, then touch up the paint. But perhaps not if it passes all above tests.
Part of the reason I am saying the above is that the top tube is not the highest stressed part of the frame, and that's a pretty fat tube. That kind of damage on skinny chainstay or seatsay, would be more critical. Not saying the above is "fine", but you have a bit more margin.
What style of bike is it? Road? Mountain? Downhill?
#17
Full Member
Thread Starter
Join Date: Mar 2013
Location: Albany, NY
Posts: 420
Bikes: Trek FX 7.3, Specialized Roubaix, Orbea Terra, Aostimotor S17 ebike, Huffy RedRock (first bike)
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 205 Post(s)
Liked 268 Times
in
134 Posts
Sorry forgot to mention, it's a Bianchi Vertigo with 105 components, appears around 2014. I don't think it's worth repairing either to flip or ride (too small). I was planning to acquire a gravel frame and stick fatter tires on those wheels or sell parts. I drive past CK Bicycles every day, which is one of repair facilities squirtdad mentioned, hoping they can scan it for little money.
#18
Senior Member
Join Date: Dec 2004
Posts: 1,098
Mentioned: 2 Post(s)
Tagged: 0 Thread(s)
Quoted: 559 Post(s)
Liked 648 Times
in
381 Posts
What's the price of the frame failing?
Are you willing to pay that price?
I know of only a few people I'd trust with repairing CF.
And they would tell me to get a new frame.
Are you willing to pay that price?
I know of only a few people I'd trust with repairing CF.
And they would tell me to get a new frame.
#19
Senior Member
Join Date: Aug 2009
Posts: 1,817
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 504 Post(s)
Liked 634 Times
in
374 Posts
Reminds me of my boat building days - a company I briefly worked for built commercial fishing boats, in order to be eligible for a government grant they required clear gelcoat below the waterline. Some genius started a layup with full coloured gelcoat, not just above the waterline, and nobody thought to question this until they opened the mould to find ... a hull they couldn't sell. Fortunately I soon found employment with a less stupid outfit.
#20
Senior Member
Join Date: May 2010
Location: Bastrop Texas
Posts: 4,485
Bikes: Univega, Peu P6, Peu PR-10, Ted Williams, Peu UO-8, Peu UO-18 Mixte, Peu Dolomites
Mentioned: 13 Post(s)
Tagged: 0 Thread(s)
Quoted: 969 Post(s)
Liked 1,631 Times
in
1,047 Posts
Just like with any boat hull or any other composite object: use a hard object to tap along the carbon top tube. It should have a hard crisp knock to it. When you get to that chipped section, does the tone change? If there is no change in tone then I would say it's totally fine. If it turns into a thud then there is de-lamination.
I dont know if its practical but thinking more along this line it might be a good idea to ping/thump your new carbon bikes and get familiar with thier sound. That way you could identify changes latter on.
I dont know if people already do this...
Note: My backyard DIY repair of this injury would be to strip the paint and after close inspection graft on a long aluminum sleeve over the tube.
__________________
No matter where you're at... There you are... Δf:=f(1/2)-f(-1/2)
No matter where you're at... There you are... Δf:=f(1/2)-f(-1/2)
Last edited by zandoval; 02-07-24 at 11:44 AM.
#21
Senior Member
Join Date: Apr 2019
Location: UK
Posts: 1,404
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 682 Post(s)
Liked 453 Times
in
338 Posts
I had similar damage in a chainstay fixed by the guys at Carbon Bike Repair who pop up on youtube from time to time. £300. Another 300 for paint. £50 each end to remove and redo all cabling. Completely invisible but the bike was worth a lot more than this one.
Likes For CrimsonEclipse:
#24
Senior Member
Join Date: Aug 2009
Posts: 1,817
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 504 Post(s)
Liked 634 Times
in
374 Posts
Oh, I know the type, while in the Navy, when the ship pulled into the yards for maintenance one time, 3 of us from deck were "lent" to the boat maintenance "shack" led by a salty old civilian who didn't even know what PPE was, we were there to refurbish our 2 boats, but he had us doing all sorts of things, learned a lot, but went out and bought me a rtespirator, and other PPE for the second day. Turned out well, as the guys on the ship were getting off around 4-6 pm, we left much earlier, and had most Fridays off. Not a bad 3 months, and now I can roll awlgrip with the best of them.