Is this cracked titanium frame safe to ride?
#152
Senior Member
Join Date: May 2017
Location: Hacienda Hgts
Posts: 2,106
Bikes: 1999 Schwinn Peloton Ultegra 10, Kestrel RT-1000 Ultegra, Trek Marlin 6 Deore 29'er
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 822 Post(s)
Liked 1,960 Times
in
943 Posts
At least the OP does not have to wear a helmet if he rides his bike with a cracked headtube "hard."
#153
Friendship is Magic
Join Date: Nov 2010
Location: Sacramento, CA
Posts: 22,984
Bikes: old ones
Mentioned: 304 Post(s)
Tagged: 0 Thread(s)
Quoted: 26402 Post(s)
Liked 10,374 Times
in
7,203 Posts
TIG Welding a Titanium Bike Frame
...there was a short afternoon workshop on working with titanium frames, at the NAHBS here about ten years ago.It's a lot harder to do a good job than you might initially think, if you're mostly familiar with welding steel and aluminum.
Mostly the gas shielding arrangements are more complex, to prevent contamination of the weld.
__________________
#154
Friendship is Magic
Join Date: Nov 2010
Location: Sacramento, CA
Posts: 22,984
Bikes: old ones
Mentioned: 304 Post(s)
Tagged: 0 Thread(s)
Quoted: 26402 Post(s)
Liked 10,374 Times
in
7,203 Posts
There are three types or cracks in titanium frames (from best to worst):
- Weld crack
- seam crack (titanium comes in sheets that are bent into tubes and seam welded.)
- Stress crack
With the exception of watching the lecture at NAHBS, I have never considered welding titanium. I guess it's possible that training of the average machine shop welder has progressed significantly, but I'm dubious. I actually did first learn welding at a Votec outside of Charleston, S.C., but they were mostly tuning out welders for the shipyard there. So we ran beads on steel plate with heavy duty stick welder for hours and hours. Maybe Votec education has changed since then too, but it would need to have changed a lot.
It's not just running a bead on your crack, and getting full penetration. There's also the issue of gas shielding the interior of the head tube, as the weld progresses.
If this were easy, there would probably be more people doing it.
__________________
Likes For 3alarmer:
#155
ignominious poltroon
Join Date: Jan 2022
Posts: 4,034
Mentioned: 3 Post(s)
Tagged: 0 Thread(s)
Quoted: 2238 Post(s)
Liked 3,429 Times
in
1,793 Posts
You could stockpile several pints of your own blood for future transfusions, should the weld not hold.
Likes For Polaris OBark:
#156
Senior Member
Join Date: Sep 2017
Posts: 7,872
Mentioned: 38 Post(s)
Tagged: 0 Thread(s)
Quoted: 6958 Post(s)
Liked 10,960 Times
in
4,686 Posts
https://bicycles.stackexchange.com/q...-advice-needed
With the exception of watching the lecture at NAHBS, I have never considered welding titanium. I guess it's possible that training of the average machine shop welder has progressed significantly, but I'm dubious. I actually did first learn welding at a Votec outside of Charleston, S.C., but they were mostly tuning out welders for the shipyard there. So we ran beads on steel plate with heavy duty stick welder for hours and hours. Maybe Votec education has changed since then too, but it would need to have changed a lot.
It's not just running a bead on your crack, and getting full penetration. There's also the issue of gas shielding the interior of the head tube, as the weld progresses.
If this were easy, there would probably be more people doing it.
With the exception of watching the lecture at NAHBS, I have never considered welding titanium. I guess it's possible that training of the average machine shop welder has progressed significantly, but I'm dubious. I actually did first learn welding at a Votec outside of Charleston, S.C., but they were mostly tuning out welders for the shipyard there. So we ran beads on steel plate with heavy duty stick welder for hours and hours. Maybe Votec education has changed since then too, but it would need to have changed a lot.
It's not just running a bead on your crack, and getting full penetration. There's also the issue of gas shielding the interior of the head tube, as the weld progresses.
If this were easy, there would probably be more people doing it.
Likes For Koyote:
#157
Junior Member
I agree it was dishonest. However, to be completely objective, I didn't pay anywhere near the value of an undamaged frame. The seller clearly priced the bike taking the damage into consideration. Furthermore, the fact that it was priced so low should have sparked suspicion, and led to a more thorough inspection prior to purchase. The onus falls upon me to conduct one when engaging in a transaction with a random FB marketplace seller.
#158
Tragically Ignorant
Join Date: Jun 2018
Location: New England
Posts: 15,613
Bikes: Serotta Atlanta; 1994 Specialized Allez Pro; Giant OCR A1; SOMA Double Cross Disc; 2022 Allez Elite mit der SRAM
Mentioned: 62 Post(s)
Tagged: 0 Thread(s)
Quoted: 8186 Post(s)
Liked 9,098 Times
in
5,054 Posts
Likes For livedarklions:
#159
Tragically Ignorant
Join Date: Jun 2018
Location: New England
Posts: 15,613
Bikes: Serotta Atlanta; 1994 Specialized Allez Pro; Giant OCR A1; SOMA Double Cross Disc; 2022 Allez Elite mit der SRAM
Mentioned: 62 Post(s)
Tagged: 0 Thread(s)
Quoted: 8186 Post(s)
Liked 9,098 Times
in
5,054 Posts
As previously stated, I purchased a titanium frame with a minor dent for dirt cheap 5 years ago. It's been lovely and is my favorite bike. Every member here who gave an opinion advised against purchasing it. It's similar to when I tell people I drive old cars to avoid car payments and they start clucking about safety standards. We've become a society of pampered wusses.
I went and checked the tape from 2017, you're either remembering wrong or you're a damn liar:
https://www.bikeforums.net/19850083-post32.html
#160
Senior Member
Join Date: Dec 2020
Location: Wake Forest, NC
Posts: 5,783
Bikes: 1989 Cinelli Supercorsa
Mentioned: 11 Post(s)
Tagged: 0 Thread(s)
Quoted: 3504 Post(s)
Liked 2,924 Times
in
1,774 Posts
Seven pages. Seven...pages.
And my initial question still hasn't been answered in any serious way (Although someone mis-interpreted that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
And my initial question still hasn't been answered in any serious way (Although someone mis-interpreted that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
Last edited by smd4; 09-06-22 at 06:16 AM.
Likes For smd4:
#161
Full Member
Thread Starter
Seven pages. Seven...pages.
And my initial question still hasn't been answered in any serious way (Although someone morphed that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
And my initial question still hasn't been answered in any serious way (Although someone morphed that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
#162
Full Member
Thread Starter
I went and checked the tape from 2017, you're either remembering wrong or you're a damn liar:
https://www.bikeforums.net/19850083-post32.html
https://www.bikeforums.net/19850083-post32.html
#163
Senior Member
Join Date: Dec 2020
Location: Wake Forest, NC
Posts: 5,783
Bikes: 1989 Cinelli Supercorsa
Mentioned: 11 Post(s)
Tagged: 0 Thread(s)
Quoted: 3504 Post(s)
Liked 2,924 Times
in
1,774 Posts
#164
Senior Member
Join Date: Dec 2020
Location: Wake Forest, NC
Posts: 5,783
Bikes: 1989 Cinelli Supercorsa
Mentioned: 11 Post(s)
Tagged: 0 Thread(s)
Quoted: 3504 Post(s)
Liked 2,924 Times
in
1,774 Posts
I think my favorite is from Ms. Raqball, who initially said (referring to a question I asked):
But then later, seemed to be OK will someone riding the bike (as long as it wasn't ridden "hard"):
You are giving TERRIBLE and UNSAFE advice...
Yeah I would not push it hard though.
#165
Senior Member
Join Date: Apr 2021
Posts: 4,083
Mentioned: 6 Post(s)
Tagged: 0 Thread(s)
Quoted: 2333 Post(s)
Liked 2,097 Times
in
1,314 Posts
Is this cracked titanium frame safe to ride?
No.
I thought my first response was a nice way of saying, "no"
What is your definition of safety? To me, it is freedom from unacceptable risk. What is risk? It is a combination of the probability of failure and severity of such a failure.
If the front end fails, you are forked.
Were you expecting a professionally done FMEA? If so, my hourly rate is $450
I thought my first response was a nice way of saying, "no"
What is your definition of safety? To me, it is freedom from unacceptable risk. What is risk? It is a combination of the probability of failure and severity of such a failure.
If the front end fails, you are forked.
Were you expecting a professionally done FMEA? If so, my hourly rate is $450
Seven pages. Seven...pages.
And my initial question still hasn't been answered in any serious way (Although someone mis-interpreted that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
And my initial question still hasn't been answered in any serious way (Although someone mis-interpreted that question into "advice"). We've got lots of predictions of end-result catastrophic failure, hoped-for good dental insurance, impending death...But no theories about the actual process of frame failure that will lead to all of this.
Seven pages.
"Crack, crash." Uh huh.
What do you think that means? Do you think the crack will propagate the entire length of the head tube? If so, will it then roll open? Or will the front end get so wobbly that the rider will then deicide to stop? Will the crack stop at the reinforcing ring at the top?
Lots of fear mongering. Not much actual thought.
(Why should I be surprised? People still think my rims are going to explode at 140 psi).
#166
Senior Member
Join Date: Dec 2020
Location: Wake Forest, NC
Posts: 5,783
Bikes: 1989 Cinelli Supercorsa
Mentioned: 11 Post(s)
Tagged: 0 Thread(s)
Quoted: 3504 Post(s)
Liked 2,924 Times
in
1,774 Posts
No.
I thought my first response was a nice way of saying, "no"
What is your definition of safety? To me, it is freedom from unacceptable risk. What is risk? It is a combination of the probability of failure and severity of such a failure.
If the front end fails, you are forked.
Were you expecting a professionally done FMEA? If so, my hourly rate is $450
I thought my first response was a nice way of saying, "no"
What is your definition of safety? To me, it is freedom from unacceptable risk. What is risk? It is a combination of the probability of failure and severity of such a failure.
If the front end fails, you are forked.
Were you expecting a professionally done FMEA? If so, my hourly rate is $450
#167
Senior Member
Join Date: Apr 2021
Posts: 4,083
Mentioned: 6 Post(s)
Tagged: 0 Thread(s)
Quoted: 2333 Post(s)
Liked 2,097 Times
in
1,314 Posts
Likes For GhostRider62:
#168
Senior Member
Join Date: Dec 2020
Location: Wake Forest, NC
Posts: 5,783
Bikes: 1989 Cinelli Supercorsa
Mentioned: 11 Post(s)
Tagged: 0 Thread(s)
Quoted: 3504 Post(s)
Liked 2,924 Times
in
1,774 Posts
You just can't explain to me what this "catastrophic failure" will look like? How is asking this question "trolling?" You can't describe it. Not even a guess. Amazing. Even I wrote down some examples. Why don't you just grab one I wrote and suggest it?
#170
Senior Member
Join Date: Jan 2010
Posts: 39,232
Mentioned: 211 Post(s)
Tagged: 1 Thread(s)
Quoted: 18409 Post(s)
Liked 15,528 Times
in
7,325 Posts
Likes For indyfabz:
#171
Tragically Ignorant
Join Date: Jun 2018
Location: New England
Posts: 15,613
Bikes: Serotta Atlanta; 1994 Specialized Allez Pro; Giant OCR A1; SOMA Double Cross Disc; 2022 Allez Elite mit der SRAM
Mentioned: 62 Post(s)
Tagged: 0 Thread(s)
Quoted: 8186 Post(s)
Liked 9,098 Times
in
5,054 Posts
No, but there are plenty of people saying essentially just make sure the dent didn't affect the geometry and if not, it's probably ok. That's an opinion, and it's not "don't buy the bike". So the post I was responding to was either just wrong or a deliberate lie.
Sorry, but this ask for advice then trash people because you don't like the advice troll is absolutely the most annoying bit on BF.
No one really knows what that crack is likely to do because it's not an experiment anyone is currently running. Honestly, you probably won't get hurt if/when the thing goes completely, but it's definitely a possibility. Honestly, at this piouint, I don't care if you break your neck because you know full well you're taking that risk. You want to call people wusses because they won't? You get no good will from anyone at that point. I can't imagine why anyone would want to spend the time to give you reasoned advice after that.
Likes For livedarklions:
#172
Senior Member
Join Date: Jan 2005
Location: Baltimore, MD
Posts: 5,371
Mentioned: 15 Post(s)
Tagged: 0 Thread(s)
Quoted: 2482 Post(s)
Liked 2,952 Times
in
1,677 Posts
Here's a guy who used the drill-and-clamp method. Maybe you can find a similar clamp of appropriate inner and outer diameters.
Note that titanium is difficult to drill. Look up advice on drilling it properly.
Note that titanium is difficult to drill. Look up advice on drilling it properly.
Likes For Trakhak:
#173
Senior Member
Join Date: Sep 2017
Posts: 7,872
Mentioned: 38 Post(s)
Tagged: 0 Thread(s)
Quoted: 6958 Post(s)
Liked 10,960 Times
in
4,686 Posts
Did I get a good deal on this Craig's List bike?
No, you got a bad deal.
Well, f--- you!
Does this bike fit me? (Insert photo of person on a bike this is grossly undersized.)
No, that bike looks a wee bit too small for you.
Well, f--- you!
This motorist did something bad to me.
No, that was your fault.
Well, f--- you!
Likes For Koyote:
#174
Junior Member
Join Date: Aug 2016
Posts: 100
Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 46 Post(s)
Likes: 0
Liked 9 Times
in
8 Posts
Precisely. This is why the OP's very casual statement below (as well as some other posters' suggestions -- I got a particular laugh at the one who suggested taking the frame to the local high school) is so ridiculous. I've known plenty of people who can weld steel, and even a few who have welding gear in their garages. Titanium is a whole different animal, though. That's why the crack shown in the OP's photo is almost certainly fatal.
Look - the OP wants to stress relieve the crack and run a worm clamp around it. At that point, even if the local weldor can't run a line of dimes, it has to be a better than not fixing it or using an external clamp. Best case, he's able to fit the headset and the headtube doesn't explode. Worst case, he has wall-art.
#175
Senior Member
Join Date: Apr 2021
Posts: 4,083
Mentioned: 6 Post(s)
Tagged: 0 Thread(s)
Quoted: 2333 Post(s)
Liked 2,097 Times
in
1,314 Posts
As if we can divine the additional stresses in the steerer tube or know whether it is carbon, steel or heavens forbid, aluminum. The forces are meant to be taken at the crown and bearings, not laterally on the steerer tube as that crack propagates. And how fast will it propogate?
The couple of riders I know with failed front ends required close to a year of rehab.
If the crack was in another location, I might get it fixed but then again I do have such a frame and decided not have it repaired. So, it is a double no for me
The couple of riders I know with failed front ends required close to a year of rehab.
If the crack was in another location, I might get it fixed but then again I do have such a frame and decided not have it repaired. So, it is a double no for me
Likes For GhostRider62: