How to remove anodizing?

Old 06-30-22, 03:48 PM
  #1  
Lbxpdx
Full Member
Thread Starter
 
Join Date: Oct 2020
Location: Portland
Posts: 359
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 161 Post(s)
Likes: 0
Liked 267 Times in 98 Posts
How to remove anodizing?

I salvaged some old XT thumb shifters and brake levers for a rebuild, but the black anodizing is terribly faded. What is the preferred method of removing the anodizing?


Lbxpdx is offline  
Old 06-30-22, 04:14 PM
  #2  
Chombi1 
Senior Member
 
Chombi1's Avatar
 
Join Date: Nov 2015
Posts: 4,457
Mentioned: 102 Post(s)
Tagged: 0 Thread(s)
Quoted: 1629 Post(s)
Likes: 0
Liked 814 Times in 527 Posts
Better double check whether that's anodizing or just black paint.......
__________________
72 Line Seeker
83 Davidson Signature
84 Peugeot PSV
84 Peugeot PY10FC
84 Gitane Tour de France.
85 Vitus Plus Carbone 7
86 ALAN Record Carbonio
86 Medici Aerodynamic (Project)
88 Pinarello Montello
89 Bottecchia Professional Chorus SL
95 Trek 5500 OCLV (Project)
Chombi1 is offline  
Old 06-30-22, 04:14 PM
  #3  
Lbxpdx
Full Member
Thread Starter
 
Join Date: Oct 2020
Location: Portland
Posts: 359
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 161 Post(s)
Likes: 0
Liked 267 Times in 98 Posts
Originally Posted by Chombi1
Better double check whether that's anodizing or just black paint.......
It is a mix.
Lbxpdx is offline  
Old 06-30-22, 04:41 PM
  #4  
rjhammett
Senior Member
 
rjhammett's Avatar
 
Join Date: Dec 2011
Location: Saint Paul, Minnesota
Posts: 2,405

Bikes: 85 De Rosa, 92 Merckx MX Leader, 99 Tommasini Sintesi, 08 Look 585, 89 Merckx Corsa Extra, 72 Holdsworth Professional

Mentioned: 18 Post(s)
Tagged: 0 Thread(s)
Quoted: 362 Post(s)
Liked 549 Times in 241 Posts
I have used Drano (I use Target equivalent) to remove anodizing. I put some Drano in a zip lock bag along with the part. Watch it carefully because it doesn't take to long. I then put it in water with baking soda to neutralize it then rinse it off well.
rjhammett is offline  
Likes For rjhammett:
Old 06-30-22, 04:50 PM
  #5  
merziac
Senior Member
 
merziac's Avatar
 
Join Date: Oct 2015
Location: PDX
Posts: 14,101

Bikes: Merz x 5 + Specialized Merz Allez x 2, Strawberry/Newlands/DiNucci/Ti x3, Gordon, Fuso/Moulton x2, Bornstein, Paisley,1958-74 Paramounts x3, 3rensho, 74 Moto TC, 73-78 Raleigh Pro's x5, Marinoni x2, 1960 Cinelli SC, 1980 Bianchi SC, PX-10 X 2

Mentioned: 267 Post(s)
Tagged: 0 Thread(s)
Quoted: 4494 Post(s)
Liked 6,300 Times in 3,633 Posts
Lbxpdx

I soak in the cleaner and dip in water, scrub very carefully with stainless brush, gloves and resoak as needed.

If its a mix, acetone, stripper would be my first assault.
merziac is offline  
Old 06-30-22, 05:11 PM
  #6  
Steel Charlie
Senior Member
 
Steel Charlie's Avatar
 
Join Date: Apr 2009
Posts: 902
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 355 Post(s)
Liked 489 Times in 261 Posts
Zepp to strip the anno. Check YouTube. And search anodizing on this forum

Citrastrip for th paint
Steel Charlie is offline  
Likes For Steel Charlie:
Old 07-01-22, 08:31 AM
  #7  
gugie 
Bike Butcher of Portland
 
gugie's Avatar
 
Join Date: Jul 2014
Location: Portland, OR
Posts: 11,641

Bikes: It's complicated.

Mentioned: 1299 Post(s)
Tagged: 0 Thread(s)
Quoted: 4670 Post(s)
Liked 5,769 Times in 2,272 Posts
I stripped hard anodizing from a pair of rims once.

Never again. Once you remove the anodizing, you'll have a mottled mess, and you'll want to polish the parts. Polishing will hold up fine until you sweat on them, and then they'll look mottled again.
__________________
If someone tells you that you have enough bicycles and you don't need any more, stop talking to them. You don't need that kind of negativity in your life.
gugie is offline  
Old 07-01-22, 08:36 AM
  #8  
randyjawa 
Senior Member
 
randyjawa's Avatar
 
Join Date: Apr 2007
Location: Thunder Bay, Ontario, Canada - burrrrr!
Posts: 11,672

Bikes: 1958 Rabeneick 120D, 1968 Legnano Gran Premio, 196? Torpado Professional, 2000 Marinoni Piuma

Mentioned: 210 Post(s)
Tagged: 0 Thread(s)
Quoted: 1370 Post(s)
Likes: 0
Liked 1,743 Times in 934 Posts
I use Extra Strength Eazy Off. Slap on some EO, wait a few minutes (two to three tops) and wipe/water wash the goo off. Repeat as required. Caution - if you leave the EO on too long it will attack the aluminum alloy and that would be an unsolvable problem. Good luck.
__________________
"98% of the bikes I buy are projects".
randyjawa is offline  
Likes For randyjawa:
Old 07-01-22, 09:50 AM
  #9  
mgopack42 
Senior Member
 
Join Date: Apr 2018
Location: Los Banos, CA
Posts: 900

Bikes: 2020 Argon 18 Krypton Pro, 1985 Masi 3V Volumetrica, 3Rensho Super Record Aero, 2022 Trek District 4.

Mentioned: 23 Post(s)
Tagged: 0 Thread(s)
Quoted: 342 Post(s)
Liked 421 Times in 205 Posts
Originally Posted by rjhammett
I have used Drano (I use Target equivalent) to remove anodizing. I put some Drano in a zip lock bag along with the part. Watch it carefully because it doesn't take to long. I then put it in water with baking soda to neutralize it then rinse it off well.
I just wanted to say, that since Drano is lye (sodium hydroxide) which is a strong base, baking soda (a weak base) will not neutralize it. Better is to use vinegar, which is a weak (5% acetic) acid. Be careful whenever working with somethng as strong as lye.
As an aside, I have read that just pure lye from the Ace Hardware store might be better, since it doesnt have all of the additives (scents, surfactants, etc.) that Drano or Easy Off has. Anecdotaly, I have heard this helps with the blotchy, post strip apearance. I have no actual experience, but I read the internet A LOT!
mgopack42 is offline  
Old 07-01-22, 10:29 AM
  #10  
SwimmerMike 
Senior Member
 
Join Date: Aug 2020
Location: Saratoga, CA
Posts: 823

Bikes: 1981 Bianchi Specialissim, 1976 Colnago Super. 1971 Bob Jackson. 2012 Kestrel 4000. 2012 Willier. 2016 Fuji Cross 1.1

Mentioned: 25 Post(s)
Tagged: 0 Thread(s)
Quoted: 273 Post(s)
Liked 919 Times in 380 Posts
Originally Posted by randyjawa
I use Extra Strength Eazy Off. Slap on some EO, wait a few minutes (two to three tops) and wipe/water wash the goo off. Repeat as required. Caution - if you leave the EO on too long it will attack the aluminum alloy and that would be an unsolvable problem. Good luck.
I use Easy Off also. You still need to polish after, but much less work. My first attempt, which looked great when done but a lot of work, was to just sand the anodization off, then go finer and finer until I got to the final polishing compound.
Attached Images
SwimmerMike is offline  
Likes For SwimmerMike:
Old 07-01-22, 12:24 PM
  #11  
Camilo
Senior Member
 
Join Date: Apr 2007
Posts: 6,760
Mentioned: 10 Post(s)
Tagged: 0 Thread(s)
Quoted: 1107 Post(s)
Liked 1,197 Times in 758 Posts
Originally Posted by Steel Charlie
Zepp to strip the anno. Check YouTube. And search anodizing on this forum

Citrastrip for th paint
I've used Zepp per Youtube and other guides (probably found on bikeforums) and it worked easily and well.
Camilo is offline  
Old 07-02-22, 12:17 PM
  #12  
Steel Charlie
Senior Member
 
Steel Charlie's Avatar
 
Join Date: Apr 2009
Posts: 902
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 355 Post(s)
Liked 489 Times in 261 Posts
So here's what I did not that long ago

https://www.bikeforums.net/classic-v...p-success.html
Steel Charlie is offline  
Old 09-27-22, 09:26 PM
  #13  
omijay 
Newbie
 
Join Date: May 2021
Location: Montreal, QC Canada
Posts: 43

Bikes: 72' Masi, 78' Marinoni, 82' Davidson, 83' Davidson, 84' Mercian, 62 Schwinn Debutante

Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 15 Post(s)
Liked 12 Times in 9 Posts
I have looked at a number ot of these recipes form removing anadizing on the forum, and decided there had to be a safer way to do this where I did not expose myself to a bunch of caustic fumes in either my house or my garage. I am a chemist so I ran several tries on some old pieces in my lab.

Here is a detailed version of what I came up with recently after reading someone else's post a few years back about a general description of using sodium hydroxide and vinegar.

It involves two baths and the size of the bath will depend on the size of your parts you are stripping
.
1) Make an appropriate size bath of 5% w/v Sodium hydroxide- This is 5 grams per every 100 ml or 50 grams for every liter (4 cups). You can buy a pound (454 grams) of sodium hydroxide on Amazon for $12.99. So that is enough to make more or less 40 cups of the solution.
2) Make a similar size bath of vinegar, which is essentially 5-10% acetic acid. I used 10% acetic acid, but not everyone has acetic acid at their disposal. So household vinegar is a simpler solution
3) Place the part(s) in the sodium hydroxide bath for 1 minute (You will see bubbles forming don't panic, it will not explode, but there will be some heat generated)
4) Transfer the part to the acetic acid bath for 1 minute.
5) Rinse with cold water and rub with a rag to clean.
6) Place the part a second time in the sodium hydroxide bath for 1 minute.
7) Place the part a second time in the acetic acid bath for 1 minute.
8) Rinse with cold water and rub with a rag to clean.

Notes:
1) There are no fumes to worry about breathing in.
2) I would wear some plastic gloves
3) You can reuse the solutions several times, but you might want to store them in a sealed bottle. Particles will settle on the bottom so you can decant them away
4) Plan on polishing a lot if you strip the parts. Maintaining beautiful shiny bike parts requires work.
omijay is offline  
Likes For omijay:
Old 09-27-22, 10:03 PM
  #14  
reconnaissance
Junior Member
 
Join Date: Sep 2016
Location: Texas Hill Country
Posts: 143

Bikes: Trek 850, Trek 510, Cannondale 300m, Specialized Rockhopper, Stumpjumper, Bianchi Virata

Mentioned: 1 Post(s)
Tagged: 0 Thread(s)
Quoted: 47 Post(s)
Liked 112 Times in 38 Posts
Just want to point out that actual true anodizing penetrates into the surface of the aluminum and serves to prevent corrosion and also hardens the aluminum as far as the anodization penetrates. So the best course depends on what the goal is. If it is just color change, then a good, durable paint in the color of choice is best. Actual removal of the anodization, weakens the item (somewhat). There are other surface colorization methods, which aren’t actually anodization. Chipping is a condition of painted parts. Fading to lighter color, (purple, gray) is true anodization affected by sunlight.

Sorry to complicate things, but accuracy is important to some folks.
reconnaissance is offline  
Old 09-28-22, 09:50 AM
  #15  
icemilkcoffee 
Senior Member
 
icemilkcoffee's Avatar
 
Join Date: Aug 2009
Posts: 2,592
Mentioned: 13 Post(s)
Tagged: 0 Thread(s)
Quoted: 1541 Post(s)
Liked 1,702 Times in 956 Posts
Originally Posted by omijay
I have looked at a number ot of these recipes form removing anadizing on the forum, and decided there had to be a safer way to do this where I did not expose myself to a bunch of caustic fumes in either my house or my garage. I am a chemist so I ran several tries on some old pieces in my lab.

Here is a detailed version of what I came up with recently after reading someone else's post a few years back about a general description of using sodium hydroxide and vinegar.

It involves two baths and the size of the bath will depend on the size of your parts you are stripping
.
1) Make an appropriate size bath of 5% w/v Sodium hydroxide- This is 5 grams per every 100 ml or 50 grams for every liter (4 cups). You can buy a pound (454 grams) of sodium hydroxide on Amazon for $12.99. So that is enough to make more or less 40 cups of the solution.
2) Make a similar size bath of vinegar, which is essentially 5-10% acetic acid. I used 10% acetic acid, but not everyone has acetic acid at their disposal. So household vinegar is a simpler solution
3) Place the part(s) in the sodium hydroxide bath for 1 minute (You will see bubbles forming don't panic, it will not explode, but there will be some heat generated)
4) Transfer the part to the acetic acid bath for 1 minute.
5) Rinse with cold water and rub with a rag to clean.
6) Place the part a second time in the sodium hydroxide bath for 1 minute.
7) Place the part a second time in the acetic acid bath for 1 minute.
8) Rinse with cold water and rub with a rag to clean.

Notes:
1) There are no fumes to worry about breathing in.
2) I would wear some plastic gloves
3) You can reuse the solutions several times, but you might want to store them in a sealed bottle. Particles will settle on the bottom so you can decant them away
4) Plan on polishing a lot if you strip the parts. Maintaining beautiful shiny bike parts requires work.
What is the best way to mask off threaded holes or machined holes if you don't want the lye corroding the threads or precision machining?
icemilkcoffee is offline  
Old 09-28-22, 10:10 AM
  #16  
Velo Mule
Senior Member
 
Velo Mule's Avatar
 
Join Date: Dec 2016
Location: Long Island, NY
Posts: 2,097

Bikes: Trek 800 x 2, Schwinn Heavy Duti, Schwinn Traveler, Schwinn Le Tour Luxe, Schwinn Continental, Cannondale M400 and Lambert, Schwinn Super Sport

Mentioned: 14 Post(s)
Tagged: 0 Thread(s)
Quoted: 801 Post(s)
Liked 1,000 Times in 654 Posts
It looks like the brake levers that @Lbxpdx is posting a picture of looks to is painted black. The black paint is in poor condition.

Use paint remover to remove the black stuff. Follow up with sanding, Scotchbrite or similar abrasive.

It is also possible that this is powder coat, but it look like paint to me.

Whether there is anodizing on there I cannot say. But once you have the black off, you can repaint if that is your goal. If you want to get a polished finish and think that the finish is anodized then you can follow one of the above solutions.

By the way, there is a way to check if a piece of aluminum is anodized or not. Aluminum is electrically conductive. If you have a multimeter, set it to ohms and place the two probes on a the surface of the aluminum part. If the aluminum surface has no anodizing the reading will be under 2 ohms. If the part is anodized it will be well above 2 ohms, likely in the k-ohms range or higher.

Don't insert the points of the probes into the surface because the sharp point may penetrate through the anodized layer. Just touch the surface.
Velo Mule is offline  
Old 09-28-22, 10:21 AM
  #17  
Steel Charlie
Senior Member
 
Steel Charlie's Avatar
 
Join Date: Apr 2009
Posts: 902
Mentioned: 5 Post(s)
Tagged: 0 Thread(s)
Quoted: 355 Post(s)
Liked 489 Times in 261 Posts
It is always interesting to see the lengths people will go to in making something really simple really complicated.
JMO of course
Steel Charlie is offline  
Old 09-28-22, 10:36 AM
  #18  
SurferRosa
señor miembro
 
SurferRosa's Avatar
 
Join Date: Dec 2018
Location: Pac NW
Posts: 8,237

Bikes: '70s - '80s Campagnolo

Mentioned: 92 Post(s)
Tagged: 0 Thread(s)
Quoted: 3846 Post(s)
Liked 6,437 Times in 3,183 Posts
Originally Posted by gugie
I stripped hard anodizing from a pair of rims once. Never again. Once you remove the anodizing, you'll have a mottled mess, and you'll want to polish the parts. Polishing will hold up fine until you sweat on them, and then they'll look mottled again.
That's true with rims (IME). I tried it once with a rim, and it simply wasn't worth all the trouble. And who wants to keep a deanodized rim polished and looking perfect? That's a component that attracts all kinds of road mess.

On the other hand, I've found every other deanodized component super easy to keep polished and looking great. But I don't ride in the rain.
SurferRosa is offline  
Likes For SurferRosa:
Old 09-28-22, 09:05 PM
  #19  
omijay 
Newbie
 
Join Date: May 2021
Location: Montreal, QC Canada
Posts: 43

Bikes: 72' Masi, 78' Marinoni, 82' Davidson, 83' Davidson, 84' Mercian, 62 Schwinn Debutante

Mentioned: 0 Post(s)
Tagged: 0 Thread(s)
Quoted: 15 Post(s)
Liked 12 Times in 9 Posts
Originally Posted by icemilkcoffee
What is the best way to mask off threaded holes or machined holes if you don't want the lye corroding the threads or precision machining?
I tried to minimize the time the parts were exposed to either the basic or acidic conditions. I also tried to neutralize as fast as possible.

I have not had any trouble with threading after the treatment, but I see where this could be a concern on delicate threading.

One simple solution might be to fill the threads with a layer of petroleum jelly/vaseline during the treatment. This would act as a waterproof
barrier that would be easy to wipe off.

Someone might have a better idea, but this would be a cheap and safe option.
omijay is offline  
Likes For omijay:

Posting Rules
You may not post new threads
You may not post replies
You may not post attachments
You may not edit your posts

BB code is On
Smilies are On
[IMG] code is On
HTML code is Off


Thread Tools
Search this Thread

Contact Us - Archive - Advertising - Cookie Policy - Privacy Statement - Terms of Service -

Copyright © 2024 MH Sub I, LLC dba Internet Brands. All rights reserved. Use of this site indicates your consent to the Terms of Use.